Harris® 500K Al-Solder, 1 oz Flu, 1 oz Solder
- Item ID: 500K
- Min. Order Qty: 1
- Item ID: 500K
- Brand: Harris®
-
-
Harris® Al-Solder, 1 oz Flux, 1 oz Solder Net Content, Composition: 85% Tin, 15% Zinc, 20000 psi Tensile Strength, 391 deg F, 482 deg F
- Aluminum solder alloy for torch or iron
- Good color match on aluminum and zinc die cast
- Forms excellent corrosion-resistant joints on tough-to-solder aluminum alloys
- Not recommended for magnesium
- Up to 20,000 psi tensile strength
- 50% elongation in 2" (mechanical properties of bulk solder)
- Used to repair aluminum evaporators and soldering aluminum-to-copper tubing
- Conforms to the EU Reach & RoHS directive
- The kit includes 1 oz. (28 g) solder wire and 1.75 oz. (49.6 g) STAY-CLEAN® aluminum soldering flux
| Alloy Type | : | Solder |
| Chemical Composition | : | Tin 85%;Zinc 15% |
| Composition | : | 85% Tin, 15% Zinc |
| Diameter | : | Wire: 1/16" (1.59mm) |
| Elongation | : | 50% in 2" |
| Liquidus | : | 482 deg F (250 deg C) |
| ModelName | : | ALSOLDER™ |
| Net Content | : | 1 oz Flux, 1 oz Solder |
| Recommended Flux | : | Stay-Clean Aluminum Flux;Stay-Clean Flux on metals other than aluminum |
| Size | : | 1 jar ea. kit (includes 1/16" wire and 1 oz. Stay-Clean Aluminum Flux) |
| Solidus | : | 391 deg F (199 deg C) |
| Temperature Rating | : | 391 deg F, 482 deg F |
| Tensile Strength (PSI) | : | Up to 20,000 (Cu to Cu) |
| Tensile Strength | : | 20000 psi |
Harris® 500K