Harris® 45F3184 Brazing Alloy, 1/16 in Dia, 18 in L, Flux-Coated
- Item ID: 45F3184
- Min. Order Qty: 1
- : 76324
- Item ID: 45F3184
- Brand: Harris®
-
-
Harris® Brazing Alloy, 1/16 in Diameter, 18 in Length, Composition: 20 to 72% Silver, 25 to 50% Copper, 10 to 40% Zinc, 30 to 60% Potassium Fluoroborate, 10 to 35% Boric Acid, 1 to 5% Methacrylate Polymer, Water, Finish: Flux-Coated
- General purpose cadmium-free silver brazing alloy
- Excellent joint strength and ductility at moderately higher temperature with a melting range of approximately 145 deg F (63 deg C)
- Good ductility and capillary flow
- Fillet forming qualities are suitable for filling loose connections
- Recommended joint clearance of 0.003" - 0.006" (0.08mm - 0.15mm)
- Popular choice to braze copper, brass, steel and stainless steel
- Flux-coating eliminates the need for manual flux application
| Alloy Type | : | HighSilver |
| Brazing Temperature Range | : | 1370 deg F-1550 deg F (743 deg C-843 deg C) |
| Chemical Composition | : | Silver 44-46%;Copper 29-31%;Zinc 23-27%;Other (Total) 0.15% |
| Color | : | Silver to light yellow |
| Composition | : | 20 to 72% Silver, 25 to 50% Copper, 10 to 40% Zinc, 30 to 60% Potassium Fluoroborate, 10 to 35% Boric Acid, 1 to 5% Methacrylate Polymer, Water |
| Density | : | 4.79 (toz./cu.in.) |
| Diameter | : | 1/16" (1.59mm) |
| Electrical Conductivity (%IACS) | : | 18.9 |
| Finish | : | Flux-Coated |
| Fluidity Rating | : | 6.5 |
| Length | : | 18 in |
| Liquidus | : | 1370 deg F (743 deg C) |
| ModelName | : | SAFETY-SILV® 45 |
| Recommended Flux | : | No flux required. If a manual flux application is desired, Harris recommends Stay-Silv white flux. Stay-Silv black brazing flux is often used when brazing stainless steel or where heating cycles are prolonged or focused as in induction brazing. Harris Eco Smart boric acid free flux (powder or paste) is an excellent choice to promote sound brazed assemblies. |
| Recommended Joint Clearance | : | .003"-.006" (.076mm-.152mm) |
| Size | : | 4 oz. (9 stick tube) |
| Solidus | : | 1225 deg F (663 deg C) |